      Hastelloy C-4

      Hastelloy C-4 (UNS NO6455)
      Hastelloy C-4 Features and Applications Overview:
      The alloy is an austenitic low-carbon nickel-molybdenum-chromium alloy. The main difference between Nicrofer 6616 hMo and other alloys of similar chemical composition developed earlier is low carbon, silicon, iron and tungsten. This chemical composition provides excellent stability at 650-1040 ° C and improved resistance to intergranular corrosion, avoiding edge line corrosion susceptibility and weld HAZ corrosion under appropriate manufacturing conditions. Alloy used in flue gas desulfurization systems, pickling and acid regeneration plant, acetic acid and agricultural chemicals production, titanium dioxide production (chloride method), electrolytic plating.
      Hastelloy C-4 Similar brands:
      NS335 (China) W.Nr.2.4610 NiMo16Cr16Ti (Germany)
      Hastelloy C-4 Chemical composition:


      Alloy
      Grade

      %

      Ni

      Cr

      Fe

      Mo

      Nb

      Co

      C

      Mn

      Si

      S

      Cu

      Al

      Ti

      Hastelloy C-4

      Min

      Margin

      14.5


      14.0










      Maximum

      17.5

      3.0

      17.0


      2.0

      0.009

      1.0

      0.05

      0.01



      0.7

      Hastelloy C-4 Physical Properties:

      Density
      g/cm3

      Melting point

      Thermal conductivity
      λ/(W/m•℃)

      Specific heat capacity
      J/kg•℃

      Elastic Modulus
      GPa

      Shear modulus
      GPa

      Resistivity
      μΩ•m

      Poisson's ratio

      Linear expansion coefficient
      a/10-6℃-1

      8.6

      1335
      1380

      10.1(100℃)

      408

      211


      1.24


      10.9(100℃)

      Hastelloy C-4 Mechanical Properties: (minimum mechanical properties at 20 ℃):

      Heat treatment methods

      Tensile strengthσb/MPa

      Yield Strengthσp0.2/MPa

      Elongation rate σ5 /%

      Brinell hardness HBS

      Solution treatment

      690

      275

      40


      Hastelloy C-4 production standards:

      Standard

      Bar

      Forgings

      Plate (with) material

      Wire

      Pipe

      American Society for Testing and Materials

      ASTM B574

      ASTM B336

      ASTM B575


      ASTM B622
      ASTM B619
      ASTM B626

      American Aerospace Materials Technical Specification






      American Society of Mechanical Engineers

      ASME SB574

      ASME SB336

      ASME SB575


      ASTM SB622
      ASTM SB619
      ASTM SB626

      Hastelloy C-4 microstructure:

      The alloy is face-centered cubic lattice structure, its chemical composition to ensure the stability of the metallographic and anti-sensitization.

      Hastelloy C-4 process performance and requirements:

      1, In the heat treatment process can not contact with sulfur, phosphorus, lead and other low melting point metal, or the alloy will become brittle, should pay attention to remove such as marking paint, temperature indicator paint, colored crayons, lubricants, fuel and other dirt. The lower the sulfur content of the fuel the better, the sulfur content of natural gas should be less than 0.1%, the sulfur content of heavy oil should be less than 0.5%. Electric furnace heating is a better choice, because the electric furnace can accurately control the temperature and the furnace gas is clean. If the gas stove gas pure enough, you can choose.
      2, alloy thermal processing temperature range of 1080 ℃ ~ 900 ℃, cooling method for water cooling or other rapid cooling. To ensure the best corrosion resistance, heat treatment should be carried out after solution heat treatment.


    5. Previous product:None
    6. Next product:None
    7. Return to
    8.  
      News Center
      Customer Service
      Copyright © Danyang Hualong Special Steel Co., Ltd. - All rights reserved
      日韩无码黄色网址_国产午夜在线网站_亚洲欧美精品一级免费看_中文字幕亚洲第一
        1. <blockquote id="se4ra"></blockquote>
        2. <source id="se4ra"></source>
        3. <var id="se4ra"></var>